Dual Shield 110C

ESAB

Dual Shield 110C

The following items have been added to your list


x

High strength steels are increasingly being used as they offer the designer the possibility of making lighter, higher performance structures with good overall cost effectiveness together with lower environmental impacts. The use of high-strength steel can mean lower fabrication costs, increased payloads, more durable products, more effective space utilization and increased safety. Dual Shield 110C is ESAB's new all-positional, low hydrogen rutile cored wire for use with CO2 shielding gas mixtures. Designed for high integrity welding of high strength steels this wire produces tough weld metal down to -60 C and meets the low diffusible hydrogen grade of H4. The benefits of using this wire with CO2 shielding gas include availability, cost and the advantageous depth to width bead profile. Dual Shield 110C is extremely welder friendly. It is easy to obtain flat welds with good penetration and smooth wetting into the plate edges. The brittle slag is easily removed leaving a smooth weld appearance. Typical positional welding defects such as lack of fusion and slag inclusions are avoided. The wires have a high tolerance for poor joint preparation and high quality one-sided root runs can be made economically on ceramic backing. High strength steels can be difficult to weld and in order to achieve the desired mechanical properties, without defects requires strict control of the welding parameters including the weld cooling rate. If assistance is required please contact your local ESAB representative.

BUY NOW


Features

  • High strength weld metal (Yield >690MPa)
  • Excellent low temperature toughness (>47J @ -60°C)
  • Low diffusible hydrogen levels (<4ml/100g)
  • Welder friendly
  • High deposition rates in positional welding (up to 4kg/hr)


Typical Charpy V-Notch Properties

As Welded
Impact Value 60 J
Shielding Gas C1 shielding gas AWS
Testing Temperature -60 °C

Typical Tensile Properties

ConditionElongationShielding GasTensile Strength Yield Strength
As Welded18 %C1 shielding gas AWS 840 MPa761 MPa

Deposition Data

Current 100-300 A
Deposition Rate 1.3-5.8 kg/h
Diameter 1.2 mm
Voltage 21-32 V
Wire Feed Speed 3.2-14.5 m/min

Classifications

Weld Metal SFA/AWS A5.36 : E111T1-C1A6-G-H4
EN ISO 18276-A : T 69 6 Z P C 2 H5

Approvals

Grade 4YQ690 SA H5
Society ABS
Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type Low Alloy (Ni Mo)
Welding Current DC+

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C Mn Mo Ni Si
C1 Shielding gas
0.055 % 1.21 % 0.4 % 2.3 % 0.39 %
x

Part Numbers and Accessories

Part Numbers : Dual Shield 110C
Dual Shield 110C 1.2 4x5kg VP 35CK12560V FIND A DISTRIBUTOR