OK Aristorod 13.12

ESAB

OK Aristorod 13.12

The following items have been added to your list


x

OK AristoRod 13.12 is a 1.1Cr-0.5Mo-alloyed, bare, solid wire for the GMAW of creep-resistant steels of the same composition, like those used for pipes in pressure vessels and boilers with a service temperature of up to 450°C. OK AristoRod 13.12 is treated with ESAB’s unique Advanced Surface Characteristics (ASC) technology, taking MAG welding operations to new levels of performance and all-round efficiency, especially in robotic and mechanised welding. Characteristic features include excellent start properties; trouble-free feeding at high wire speeds and lengthy feed distances; a very stable arc at high welding currents; extremely low levels of spatter; low fume emission; reduced contact tip wear and improved protection against corrosion of the wire.

BUY NOW


Typical Tensile Properties

Condition As Welded PWHT Q.T. Q.T. As Welded Stress Relieved Stress Relieved
700°C 0.5h 940+730°C 15h 940+730°C 15h +
Shielding Gas EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21) EN 80Ar/20CO2 (M21)
Tensile Strength 740 MPa 580 MPa 460 MPa 410 MPa 760 MPa 500 MPa 610 MPa
Yield Strength 640 MPa 450 MPa 320 MPa 210 MPa 605 MPa 390 MPa 500 MPa
Elongation 18 % 24 % 35 % 25 % 15 % 17 % 26 %
Testing Time 0.5 hr 1 hr
Testing Temperature 700 degC 690 degC

Deposition Data

Current Deposition Rate Diameter Voltage Wire Feed Speed
80-280 A 1.0-5.4 kg/h (2-11 lb/h) 1.0 mm (0.040 in.) 18-28 V 2.7-14.7 m/min (106-579 in./min)
120-350 A 1.5-6.6 kg/h (3-14 lb/h) 1.2 mm (0.047 in.) 20-33 V 2.7-12.4 m/min (106-488 in./min)
225-480 A 3.3-11.6 kg/h (7-25 lb/h) 1.6 mm (1/16 in.) 26-38 V 3.1-12.0 m/min (122-472 in./min)
80-280 A 1.0-5.4 kg/h (2-11 lb/h) 0.8 mm (0.030 in.) 18-28 V 2.7-14.7 m/min (106-579 in./min)

Classifications

Wire Electrode SFA/AWS A5.28 : ER80S-G
EN ISO 21952-A : G CrMo1Si
EN ISO 21952-B : G 55M 1CM3
GOST 2246 : 08X CM A

Approvals

Approvals NAKS/HAKC 1.2MM
VdTÜV 10089
Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type Low Alloyed (1 % Cr, 0.5 % Mo)

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr Mn Mo Ni P S Si
0.11 % 1.18 % 1.00 % 0.42 % 0.02 % - - 0.65 %
Typical Weld Metal Analysis %
80Ar/20CO2
0.1 % 1.1 % 1.0 % 0.5 % - 0.010 % 0.015 % 0.7 %
CO2
0.09 % 1.1 % 1.0 % 0.5 % - 0.010 % 0.015 % 0.6 %
x

Part Numbers and Accessories

Part Numbers : OK Aristorod 13.12
1B12086900 FIND A DISTRIBUTOR
1B12106910 FIND A DISTRIBUTOR
1B12109320 FIND A DISTRIBUTOR
1B12126910 FIND A DISTRIBUTOR
1B12129320 FIND A DISTRIBUTOR
1B12166910 FIND A DISTRIBUTOR
x
x

x

Loading..