Exaton 19.12.3.L

Exaton

Exaton 19.12.3.L

The following items have been added to your list


x

19.12.3.L is used for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo-types, stabilized or non-stabilized, e.g. ASTM 316, 316L and 316Ti as well as 304, 304L, 321 and 347, used for service temperatures up to 400°C (750°F). It is also used for Cr steels with max. 19% Cr. It is used for MIG/MAG welding.

BUY NOW


Exaton 19.12.3.L

Documents


Typical Charpy V-Notch Properties

Impact Value Testing Temperature
as welded
75 J (56 ft-lb) -196 degC (-321 degF)
130 J (96 ft-lb) -40 degC (-40 degF)
150 J (111 ft-lb) 20 degC (68 degF)

Typical Tensile Properties

ConditionElongationTensile Strength Yield Strength
As Welded39 %610 MPa (88 ksi)500 MPa (73 ksi)

Recommended Welding Parameters

Current Voltage Wire Diameter Wire Feed Speed
40-120 A 15-19 V 0.8 mm (0.030 in.) 4.0-8.0 m/min (157-315 in./min)
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)
230-350 A 25-30 V 1.6 mm (1/16 in.) 3.0-5.0 m/min (118-197 in./min)

Classifications

Wire Electrode EN ISO 14343-A : G 19 12 3 L
SFA/AWS A5.9 : ER316L
Werkstoffnummer : 1.4430

Approvals

Grade EN 13479
Society CE
Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type Austenitic (with appr. 8 % ferrite) 19 % Cr - 12 % Ni - 3 % Mo - Low C

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr Cu FN WRC-92 Mn Mo N Nb Ni P S Si
0.015 % 18.5 % 0.1 % 9 % 1.7 % 2.6 % 0.04 % 0.02 % 12 % <0.025 % 0.015 % 0.4 %
Typical Weld Metal Analysis %
<0.02 % 18 % 0.1 % 7 % 1.7 % 2.5 % 0.05 % 0.01 % 12 % <0.03 % <0.02 % 0.4 %
x

Part Numbers and Accessories

Part Numbers : Exaton 19.12.3.L
S630089820 FIND A DISTRIBUTOR