OK Autrod 317L
A continous solid corrosion resisting chromium-nickel-molybdenum wire for welding of austenitic stainless alloys of 19% Cr 13% Ni 3% Mo types. OK Autrod 317L has a good resistance to general corrosion and pitting due to its high content of molybdenium. The alloy has a low carbon content which makes this alloy particularly recommended were there is a risk of intergranular corrosion. The alloy is used in severe corrosion conditions such as in the petrochemical , pulp and paper industries.
Typical Charpy V-Notch Properties
| as welded | ||||
Typical Tensile Properties
| Condition | Elongation | Tensile Strength | Yield Strength |
| As Welded | 45 % | 600 MPa (87 ksi) | 390 MPa (57 ksi) |
Deposition Data
| Current | Deposition Rate | Diameter | Voltage | Wire Feed Speed |
| 50-140 A | 0.8-2.7 kg/h (1.8-6.0 lb/h) | 0.8 mm (0.030 in.) | 16-22 V | 3.4-11.0 m/min (134-433 in./min) |
| 180-280 A | 2.6-4.5 kg/h (5.7-9.9 lb/h) | 1.2 mm (0.047 in.) | 20-28 V | 4.9-8.5 m/min (193-335 in./min) |
| 230-350 A | 3.0-5.2 kg/h (6.6-11. lb/h) | 1.6 mm (1/16 in.) | 24-28 V | 3.2-5.5 m/min (126-217 in./min) |
| 80-190 A | 0.9-2.7 kg/h (2.0-6.0 lb/h) | 1.0 mm (0.040 in.) | 16-24 V | 2.6-7.1 m/min (102-280 in./min) |
Classifications
| Wire Electrode |
SFA/AWS A5.9 : ER317L EN ISO 14343-A : G 18 15 3 L |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Alloy Type | Austenitic (with approx. 8 % ferrite) |
| Shielding Gas | M12, M13 (EN ISO 14175) |
Typical Weld Metal Analysis %
| Typical Wire Composition % | ||||||||||||||
| C | Cr | FN WRC-92 | Mn | Mo | N | Ni | Si | |||||||
| 0.01 % | 18.9 % | 7 % | 1.4 % | 3.6 % | 0.05 % | 13.6 % | 0.4 % | |||||||